NiCrTi Thermal Spray Wire Nickel Alloy Wire Tafa 45CT Metal Wire Deposit Rate Spray Wire High-Temperature Oxidation
Product Description
NiCrTi is very effective in providing long term protection to boiler tubes against high temperature sulfidation. The wrought material is highly resistant to sulfur/vanadium atmospheres up to 1800°F. Wrought material of this type has shown a 2 mil per year corrosion rate over a nine year period when used in the super heater section of boilers. Coatings of 45CT wire applied to boiler tubes have shown virtually no loss of thickness or spalling after 24 months of service.
Equivalent to: Tafa 45CT Metco8500, PMET889.
Surface Preparation
Surface should be clean, white metal, with no oxides (rust), dirt, grease, or oil on the surface to be coated. Note: It is best not to handle surfaces after cleaning. Recommended method of preparation is, to grit blast with 24 mesh aluminum oxide, rough grind, or rough machine in a lathe.
Chemical Composition(wt%)
| Grade | Ni | Cr | Ti |
| NiCrTi | Bal | 45 | 0.3-1.0 |
Typical Seposit Characteristics
| Typical Hardness | Bond Strength | Deposit Rate | Deposit Efficiency | Wire Coverage |
| HRC 30-35 | 7000 psi | 10 lbs/hr/100A | 85 % | 0.8 oz / ft2 / mil |
Packing Details
| Diameter | Dimension Tolerance | Packing | Wire Weight |
| 2.0mm | +0/-0.05 | D 300 Spool | 15kgs(33 lbs)/spool |
Other sizes can be produced by customers’ requirement.
Applications
· Boiler Tubes
· Corrosion Resistance
· High-temperature oxidation protection
Type We Could Offer
Thermal spray wire-Nickel based
| WL TYPE | Tafa | PMET | Metco | Size |
| WL-NiAl95/5 | 75B | 885 | 8400 | 1.6/2.0/3.17mm |
| WL-NiAl80/20 | 79B | 884 | 405 | 2.0/3.17mm |
| WL-NiCr80/20 | 06C | 821 | 8450 | 1.6/2.0/3.17mm |
| WL-Monel400 | 70T | 877 | Monel | 1.6/2.0/3.17mm |
| WL-NiCrTi | 45CT | 889 | 8500 | 1.6/2.0/3.17mm |
| WL-Inconel718 | 78T | 818 | 8718 | 1.6/2.0/3.17mm |
| WL-Inconel625 | 71T | 860 | 8625 | 1.6/2.0/3.17mm |
| WL-Alloy-C276 | 77T | 876 | 8276 | 1.6/2.0/3.17mm |
| WL-NiCrAl(P) | 73MXC | 886 | 8443 | 1.6/2.0mm |
| WL-NiCrAlY(P) | 76MXC | 887 | 884 | 1.6/2.0mm |
| WL-NiMoAl(P) | 74MXC | 888 | 8447 | 1.6/2.0mm |
Thermal spray wire-Iron based
| WL TYPE | Tafa | PMET | Metco | Size |
| WL-SS420 | 60T | 720 | Metcoloy 2 | 1.6/2.0/3.17mm |
| WL-SS304/304L | 80T | 710 | Metcoloy 1 | 1.6/2.0/3.17mm |
| WL-SS316/316L | 85T | 730 | Metcoloy 4 | 1.6/2.0/3.17mm |
| WL-FeCrAl | Alcro | 731 | | 1.6/2.0mm |
| WL-FeCrBSi(P) | 95MXC | 273 | | 1.6/2.0mm |
| WL-FeCrNiB(P) | 96MXC | | | 1.6/2.0mm |
| WL-Tungsten Carbide(P) | 97MXC | 297 | Duocor | 1.6/2.0mm |
| WL-LCr Carbide(P) | 98MXC | 223 | | 1.6/2.0mm |
| WL-FeAl(P) | 35MXC | 50 | | 1.6/2.0mm |
| WL-HCr Carbide(P) | | 226 | Sm8222 | 1.6/2.0mm |
Thermal spray wire-Copper based
| WL TYPE | Tafa | PMET | Metco | Size |
| WL-Pure Copper | | | | 1.6/2.0/3.17mm |
| WL-CuSn1 | 05T | | | 1.6/2.0/3.17mm |
| WL-CuAl8 | | | Sprabronze AB | 1.6/2.0/3.17mm |
| WL-CuAl10 | 10T | 590 | Sprabronze AA | 1.6/2.0/3.17mm |
Thermal spray wire-Zinc & Aluminium based
| WL TYPE | Tafa | PMET | Metco | Size |
| WL-Pure Al | 01T | 699 | Aluminum | 1.6/2.0/3.17mm |
| WL-Pure Al Grade 1100 | | | | 1.6/2.0/3.17mm |
| WL-Pure Zn | 02Z | 540 | Zinc | 1.6/2.0/3.17mm |
| WL-AlMg5 | | | Metco AlMg | 1.6/2.0/3.17mm |
| WL-ZnAl85/15 | 02A | | Zn/Al | 1.6/2.0/3.17mm |
Thermal spray wire-Other based alloy
| WL TYPE | Tafa | PMET | Metco | Size |
| WL-Molybdenum wire | 13T | 899 | Sprabond | 1.6/2.0/3.17mm |
| WL-Babbitt wire | 04T | 542 | Sprababbitt | 1.6/2.0/3.17mm |
| WL-Tin wire | 02W | 549 | Metco Tin | 1.6/2.0mm |
| WL-Ti wire | 14T | | | 1.6/2.0mm |